Estudo in vitro: microinfiltração marginal em restaurações com resina composta classe II
DOI:
https://doi.org/10.35622/j.ram.2023.01.002Keywords:
ionomeric base, marginal microfiltration, dentistry, composite resinAbstract
Objective: to evaluate in vitro marginal microleakage in class II composite resin restorations in posterior teeth. Method: A quasi-experimental design study of longitudinal section was carried out, the sample consisted of 40 healthy upper and lower posterior teeth (premolars and molars), these were extracted for orthodontic or periodontal indications and have been preserved in distilled water for 48 hours; Those teeth that had occlusal restorations or any alteration in shape or structure were excluded. The teeth were randomly distributed in 02 experimental groups. Experimental group 1 (GE1) received the restoration with class II composite resin with ionomer base and experimental group 2 (GE2) received the restoration with class II composite resin without ionomer base. Results: when comparing the degree of marginal microleakage between GE1 and GE2 at 48 hours, 15 days, 30 days and 45 days with a confidence level of 95%, there is a statistically significant difference (p < 0.05), that is to say that, there is a higher degree of marginal microleakage in restorations with class II composite resin without ionomer base. Conclusion: Class II composite resin restorations in posterior teeth that did not have an ionomeric base have a higher degree of marginal microleakage.
References
Verdugo MD. Microfiltración marginal en restauraciones de resina empleando dos clases de ionómero de vidrio como base en la técnica sándwich [Tesis]. Quito: Universidad Central del Ecuador; 2016. 85 p.
Vivanco-Ludeña DD, Valarezco-Bravo TL. Sellado marginal en restauraciones directas con resina después del uso de gel enzimático de papaína vs sistema rotatorio para remoció de caries. Odontol (Habana). 2021;23(1).
Echeverria-Rodriguez R. Análisis comparativo del sellado marginal de restauraciones de resina compuesta convencional (Z-350 3M ESPE) y una monoincremental (Filtek Bulk Fill 3M ESPE) [Tesis]. Santiago: Universidad Finis Terrae; 2015. 47 p.
Moreno-Espinoza JO. Efectividad clínica del ionómero de vidrio híbrido en molares permanentes con MIH y caso clínico [Tesis]. Baja California: Universidad Autónoma de Baja California; 2019. 93 p.
Gupta KV, Verma P, Trivedi A. Evaluation of Microleakage of Various Restorative Materials: An in Vitro Study. J Life Sci [Internet]. 2011 Jul;3(1):29–33. Available from: https://www.tandfonline.com/doi/full/10.1080/09751270.2011.11885166 DOI: https://doi.org/10.1080/09751270.2011.11885166
Chaple-Gil AM. Técnica modificada de restauración de cavidades Clase II utilizando resinas compuestas. Rev Habanera Ciencias Medicas. 2015;14(3):337–47.
Gigoux-Koch N. Estudio comparativo in vitro del sellado marginal de restauraciones indirectas cementadas con diferentes tipos de cementos de resina compuesta existentes en el mercado nacional [Tesis]. Santiago: Universidad Finis Terrae; 2013. 74 p.
Rojas-Padilla SV, Ríos-Caro TE. Microfiltración marginal de resinas de relleno masivo y nanohíbrida en molares deciduos. Rev Cuba Estomatol. 2021;58(2):e3278.
Herrera-Raya S, Sánchez Some F, Reyes Missett G, Vázquez Rodriguez E, Guerrero Ibarra J. Microfiltración en restauraciones de resina realizadas con diferentes sitemas adhesivos estudio In Vitro. Rev Odontol Latinoam. 2016;8(2):41–5.
Ehrmantraut Nogales M, Terrazas Soto P, Leiva Buchi M. Sellado marginal en restauraciones indirectas, cementadas con dos sistemas adhesivos diferentes. Rev clínica periodoncia, Implantol y Rehabil oral [Internet]. 2011 Dec;4(3):106–9. Available from: http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0719-01072011000300004&lng=en&nrm=iso&tlng=en DOI: https://doi.org/10.4067/S0719-01072011000300004
Retamal A, Retamal J, Bader Mattar M. Análisis comparativo in vitro del grado de filtración marginal de restauraciones de resina compuesta realizadas con dos métodos de grabado ácido distintos. Rev clínica periodoncia, Implantol y Rehabil oral [Internet]. 2014 Apr;7(1):8–11. Available from: http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0719-01072014000100002&lng=en&nrm=iso&tlng=en DOI: https://doi.org/10.4067/S0719-01072014000100002
Mazumdar P, Das A, Das U. Comparative evaluation of microleakage of three different direct restorative materials (Silver Amalgam, Glass Ionomer Cement, Cention N), in Class II restorations using stereomicroscope: An In vitro Study. Indian J Dent Res [Internet]. 2019;30(2):277. Available from: http://www.ijdr.in/text.asp?2019/30/2/277/259227 DOI: https://doi.org/10.4103/ijdr.IJDR_481_17
Salih AA, Hussain ZM. Gingival Marginal Leakage of Different Tooth Colored Materials Combination as an Intermediate Layer in Class II Composite Restoration : A Comparative in Vitro Study. J Baghdad Coll Dent [Internet]. 2016 Dec;28(4):43–8. Available from: http://platform.almanhal.com/CrossRef/Preview/?ID=2-96440 DOI: https://doi.org/10.12816/0033209
Cáceres Díaz LM, Núñez H, Perdomo M. Evaluación de la microfiltración en restauraciones con resina Clase I. Rev Estomatológica Hered [Internet]. 2021 Dec 23;31(4):242–7. Available from: https://revistas.upch.edu.pe/index.php/REH/article/view/4091 DOI: https://doi.org/10.20453/reh.v31i4.4091
Bilgrami A, Alam MK, Qazi FUR, Maqsood A, Basha S, Ahmed N, et al. An In-Vitro Evaluation of Microleakage in Resin-Based Restorative Materials at Different Time Intervals. Polymers (Basel) [Internet]. 2022 Jan 24;14(3):466. Available from: https://www.mdpi.com/2073-4360/14/3/466 DOI: https://doi.org/10.3390/polym14030466
Feiz A, Sajedi M, Jafari N, Swift E. Evaluation of microleakage in Class II composite restorations: Bonded-base and bulk-fill techniques. Dent Res J (Isfahan) [Internet]. 2021;18(1):89. Available from: http://www.drjjournal.net/text.asp?2021/18/1/89/328757 DOI: https://doi.org/10.4103/1735-3327.328757
Roque-Salamanca V. Estudio comparativo In Vitro del grado de microfiltración marginal de resinas compuestas fotopolimerizables precalentadas y a temperatura ambiente en restauraciones clase II [Tesis]. Tacna: Universidad Nacional Jorge Basadre Grohmann; 2019.
León Cáceres ME, Mederos Gómez M, Cuevas Suárez CE, Maglione García F, Grazioli Pita GS. Estudio in vitro de la relación entre resistencia de unión a esmalte dental y microfiltración en resinas compuestas fotopolimerizables. Odontoestomatologia [Internet]. 2020 Jun 6;22(35):38–49. Available from: https://odon.edu.uy/ojs/index.php/ode/article/view/311 DOI: https://doi.org/10.22592/ode2020n35a6
Ullón Alcívar CP. Estudio de la microfiltración en restauraciones de resina de composite con y sin base cavitaria de ionómero de vidrio [Tesis]. Guayaquil: Universidad de Guayaquil; 2014. 93 p.
Rosero-Mendoza JC, Mendoza-Rodríguez FA, Rosero-Mendoza JI, Hernández-Yépez VA. Grado de microfiltración en restauraciones con ionomeros vidrio de base variando la secuencia en los procedimientos de restauración. Polo del Conoc [Internet]. 2017 Jun 17;2(6):1016. Available from: https://polodelconocimiento.com/ojs/index.php/es/article/view/168 DOI: https://doi.org/10.23857/pc.v2i6.168
Published
Issue
Section
License
Copyright (c) 2022 Danny Calizaya-Bendita, Fernando Chávez-Fernández , Lizeth Loaiza-Jara, Evelyn Molina-Arraya, Vilma Mamani-Cori, Ronald Poma
This work is licensed under a Creative Commons Attribution 4.0 International License.